基合金是在鈷鉻合金中熔入適量的鎢和碳，鎢的加入使鈷基體進一步固溶強化。碳在鈷中的溶解度很小，因而加入的碳和過量的鎢形成 WC，W2C，M6C等碳化物，這些硬質相彌散分布在鈷基體中，產生析出強化作用，使該類合金在800℃高溫下，仍能保持優異的高溫強度和高溫硬度，因此鈷、鉻、鎢、碳合金具有優異耐高溫磨損、抗高溫氧化和熱疲勞等綜合性能。
Cobalt-base alloy is produced by melting suitable amount of tungsten and carbon into the cobalt-chrome alloy, which will enhance the solid-solution strengthening of the cobalt base. For the low solubility of carbon in cobalt, the added carbon and superfluous tungsten may generate WC，W2C，M6C and other carbides. The hard materials distribute in the cobalt base and strengthen the separation process, thus the alloy can maintain excellent intension and rigidity under high temperature of 800℃. Thus, the cobalt, chrome, tungsten and carbon alloy have integrated perbance of preventing the high temperature wear, oxidation and thermal fatigue.
鈷在417℃溫度以下，為密排六方結構，具有低的摩擦系數，而具有很好的耐磨性。在417℃溫度時發生由密排六方晶體，向面心立方晶體的轉變，而產生體積應力。因此在噴焊時一般均需將被焊工件預熱到500℃～600℃，以防鈷基焊層開裂。
Below 417℃,cobalt is in dense-hexagonal structure,it has lower frictional coefficient and sound wear resistance. The structure of cobalt will change from dense-hexagonal crystal into face-center-cubic structure under 417℃. The volume stress may appear. Therefore, the welding pieces should be warmed up to 500℃～600℃ to avoid the crack for cobalt-base welding layers.
我公司生產的鈷基合金粉，既有適合等離子堆焊的、激光熔敷的，也有適合氧乙炔焰噴焊的，下面介紹的鈷基噴焊合金粉，采用塑料桶和鐵桶封裝，但由于粉末顆粒較細，極易吸潮，建議用戶在使用前經120℃保溫兩小時烘干后使用為佳。
Our company has different types of cobalt-base alloy powder, which can meet the requirements of laser cladding for plasma surfacing and oxyacetylene flame welding. The following cobalt-base sprayed welding alloy powder produced by our company is packaged and sealed in the plastic or bl pail. However, for the thin granularity and humidity-absorbing characteristic of the product, it’s recommended that the customer should dry the products under 120℃ for two hours before useing.