產品詳情
|
HB-YD114(Q) |
1.6 |
50-55 (受強烈沖擊后 After high impact) |
高錳鋼堆焊焊絲，受強烈沖擊后，表面具有加工硬度的特點。 High-manganese steelhardfacing flux-cored wires, and applied to repair surface of high impact wear parts, cladding layer is impacted with work hardening. |
|
HB-YD115(Q) |
1.6 |
50-55 (受強烈沖擊后After high impact) |
用于受嚴重沖擊高錳鋼堆焊，加工硬化效果顯著。 Applied to repair surface of high impact wear parts, cladding layer is impacted with work hardening. |
|
HB-YD165(Q) |
1.6 |
60-65 |
高硬度耐磨焊絲，適用于磨粒磨損表面堆焊 High hardness wear-resistant wire, it is used to abrasive wearsurfacing welding. |
|
HB-YD172(Q) |
1.6 |
≥40 |
用于堆焊齒輪、挖泥斗、礦山機械等磨損件 Applied to repair surface of high impact wear parts, such as gear aud bucket and mining machinery. |
|
HB-YD207(Q) |
1.6 |
≥50 |
用于堆焊推土機 ，螺旋槳等磨損零件 Applied to repair surface of high wear parts, such as bulldozer blade and propeller. |
|
HB-YD212(Q) |
1.2/1.6 |
≥50 |
用于堆焊各種受磨損的機件表面，如齒輪、挖斗、礦山機械 Applied to repair surface of wear parts, such as gear mud bucket and mining machinery. |
|
HB-YD256(Q) |
1.6 |
HB≥170 |
高錳鋼堆焊，適用于破碎機等受沖擊磨損部位的堆焊 High-manganese steelhardfacing flux-cored Wires,it is applied to repair surface of high impact wear parts, such as Crusher. |
|
HB-YD258(Q) |
1.6 |
55-60 |
用于耐磨表面堆焊 Applied to repair surface of wear parts. |
|
HB-YD265(Q) |
1.6 |
60-65 |
高硬度耐磨焊絲，適用于磨粒磨損表面堆焊 High hardness wear-resistant wire, it is used to abrasive wearsurfacing welding. |
|
HB-YD322(Q) |
1.6 |
≥55 |
用于堆焊各種沖模及切削刃具，兼用于修復要求耐磨損性能較高之機械零件 Applied to repair surface ofhigh wear resistanceparts, such as die and cuttingcutlery. |
|
HB-YD327A(Q) |
1.6 |
≥55 |
專門用于模具堆焊，耐磨性能高于D322 Used tomouldsurfacing, wear resistance is better than D322. |
|
HB-YD337(Q) |
1.6 |
≥48 |
用于鑄鋼或鍛鋼上堆焊鍛模 Applied to repairforging dieatcast steelorforging steel. |
|
HB-YD397(Q) |
1.6 |
≥40 |
用于堆焊鑄鋼或鍛鋼做坯體的熱鍛?；蚨押父邚姸饶湍ゼ? Applied to repair hotforging dieatcast steelor forging steel, or highstrengthwear surfacing. |
|
HB-YD405A(Q) |
1.6 |
50-59 |
用于熱軋輥開坯輥堆焊 Applied to repair hot-rolling blooming rollor. |
|
HB-YD430A(Q) |
1.6 |
20-35 |
打底層堆焊焊絲 A backing hardfacing flux-cored Wires |
|
HB-YD488A(Q) |
1.6 |
45-50 |
用于軋輥堆焊 Applied to repair rollor |
|
HB-YD507Mo(Q) |
1.6 |
35-45 |
用于510℃以下中高壓閥門堆焊 Applied to valve which operating tdivperature is less than 510℃. |
|
HB-YD518(Q) |
1.6 |
40-50 |
用于連鑄輥堆焊 Applied to repaircontinuous caster roller |
|
HB-YD688(Q) |
1.6 |
50-60 |
用于磨煤輥打底焊(韌性好，可以多層堆焊) Used to coal roller backing welding. |
|
HB-YD788(Q) |
1.6 |
55-62 |
硬度高，可以多層堆焊。 High hardness andmulti-layer welding |
|
HB-YD888(Q) |
1.2, 1.6 |
60-65 |
硬度高，堆焊層厚度不超過6mm。 High hardness, but thethicknessofsurfacing layeris less than 6mm. |
|
HB-YD888Ni(Q) |
1.2 |
58-65 |
高鉻合金焊絲，用于耐磨表面堆焊 Applied to repair surface of wear parts. |
|
HB-YD988(Q) |
1.6 |
55-63 |
高鉻合金焊絲，用于耐磨表面堆焊 Applied to repair surface of wear parts. |
|
HB-YD990(Q) |
1.6 |
55-65 |
用于高溫耐磨堆焊。 Applied to repair surface ofhigh tdivperaturewear parts. |
|
HB-YD58(Q) |
1.6 |
55-60 |
高溫耐磨焊絲，用于化推焦機磨靴的堆焊。 high tdivperaturewear hardfacing wires, |
|
HB-YD67(Q) |
1.6 |
58-63 |
用于耐磨表面堆焊 Applied to repair surface of wear parts. |
|
HB-YD95(Q) |
1.6 |
55-63 |
高鉻合金焊絲，用于耐磨表面堆焊 Applied to repair surface of wear parts. |
|
HB-DG7(Q) |
1.6 |
52-60 |
地鐵盾構施工 刃口堆焊專用，也可用于煤碳石裝載機料斗和刃口堆焊修復。 Applied to repair surface of high impact wear parts, such as shiled machine, exc ator bucket and hopper of mining machinery products. |
一、高鉻合金耐磨鑄鐵系列產品
1、各種立破、反擊破、PCK1312-1316破碎機錘頭轉子體護板，組合格板、界板，板錘，打擊板等，是選礦廠、礦廠、水泥機械最理想的耐磨配件。
2、各種高鉻合金鑄造鐵、鎢鉻鉬合金、耐火材料模具。
3、各種型號導衛板、導衛輥、成型輥、擠壓輥、冷床滾輥等。
二、耐磨合金鋼系列產品
各種型號顎破板、襯板、篩網、界板等，是選礦、礦山建陶、玄武巖礦的專用產品。
三、鑄錳13系列產品
球磨機全套配件、雷蒙機彈子、磨環、對輥、顎板、碾底、PCK1312-1316轉子體、格界板、錘頭等。
四、各種碳鋼、不銹鋼、耐熱鋼、鑄件。
五、來圖定做，設計，并承接車，刨、磨、銑床加工等業務，本廠設計PCK系列破碎機，錘頭，組合格板，界板以及各大選礦推廣使用常用破碎機錘頭材質有哪些
破碎機工作時磨料由下料斗進入破碎機腔體內，物料通過高速旋轉錘頭的碰撞來破碎物料；或者通過高度旋轉的料盤將物料甩向筒體內壁的反擊板，相撞后返回錘擊區，受到板錘錘擊而破碎物料。
目前鑄造破碎機錘頭材質有很多種，如鑄造高錳鋼系列、鑄造合金鋼系列和鑄造高鉻鑄鐵系列等。實際生產表明，各種材質制成的錘頭，使用性能差異較大，因此，錘頭材料要根據錘頭使用情況等進行合理選擇
產品適用范圍
各種型號磚機及粉碎機
注意事項
注意安裝牢固
一、高鉻合金耐磨鑄鐵系列產品
1、各種立破、反擊破、PCK1312-1316破碎機錘頭轉子體護板，組合格板、界板，板錘，打擊板等，是選礦廠、礦廠、水泥機械最理想的耐磨配件。
2、各種高鉻合金鑄造鐵、鎢鉻鉬合金、耐火材料模具。
3、各種型號導衛板、導衛輥、成型輥、擠壓輥、冷床滾輥等。
二、耐磨合金鋼系列產品
各種型號顎破板、襯板、篩網、界板等，是選礦、礦山建陶、玄武巖礦的專用產品。
三、鑄錳13系列產品
球磨機全套配件、雷蒙機彈子、磨環、對輥、顎板、碾底、PCK1312-1316轉子體、格界板、錘頭等。
四、各種碳鋼、不銹鋼、耐熱鋼、鑄件。
五、來圖定做，設計，并承接車，刨、磨、銑床加工等業務，本廠設計PCK系列破碎機，錘頭，組合格板，界板以及各大選礦推廣使用常用破碎機錘頭材質有哪些
破碎機工作時磨料由下料斗進入破碎機腔體內，物料通過高速旋轉錘頭的碰撞來破碎物料；或者通過高度旋轉的料盤將物料甩向筒體內壁的反擊板，相撞后返回錘擊區，受到板錘錘擊而破碎物料。
目前鑄造破碎機錘頭材質有很多種，如鑄造高錳鋼系列、鑄造合金鋼系列和鑄造高鉻鑄鐵系列等。實際生產表明，各種材質制成的錘頭，使用性能差異較大，因此，錘頭材料要根據錘頭使用情況等進