牌號
|
Q345A低合金結構鋼熱軋鋼板
|
|
|
|
|
|
|
|
|
|
|
|
|
|
中國ISC
|
L03451
|
|
|
|
|
|
|
|
|
|
|
|
|
|
對應標準
|
GB /T 3274-2017
|
|
|
|
|
|
|
|
|
|
|
|
|
|
碳素結構鋼和低合金結構鋼熱軋鋼板和鋼帶
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Hot-rolled plates, sheets and strips of carbon structural steels and high strength low alloy structural sheets
|
|
|
|
|
|
|
|
|
|
|
|
|
|
品牌/供貨源
|
中國大陸-> 寶鋼
|
|
|
|
|
|
|
|
|
|
|
|
|
|
歸類
|
合金鋼
|
|
|
|
|
|
|
|
|
|
|
|
|
|
性能
|
耐腐蝕 焊接性
|
|
|
|
|
|
|
|
|
|
|
|
|
|
標簽
|
熱軋鋼板和鋼帶 低合金鋼
|
|
|
|
|
|
|
|
|
|
|
|
|
|
說明
|
性能特點：
|
|
|
|
|
|
|
|
|
|
|
|
|
|
綜合力學性能好，冷熱加工性能、焊接性能和耐蝕性能均好。Q345A鋼材與Q345C，D，E鋼相比而言，低溫沖沖擊的試驗溫度高，性能差，含有害物資P,S量比Q345C,D,E要高。
|
|
|
|
|
|
|
|
|
|
|
|
|
|
用途舉例：
|
|
|
|
|
|
|
|
|
|
|
|
|
|
廣泛應用于橋梁、車輛、船舶、建筑、壓力容器等。
|
|
|
|
|
|
|
|
|
|
|
|
|
|
本標準適用于厚度不大于400mm的碳素結構鋼和低合金鋼熱軋鋼板和鋼帶
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Q345A 化學元素成分含量(%)
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
成分
|
C
|
Si
|
Mn
|
P
|
S
|
Cr
|
Ni
|
Cu
|
Mo
|
N
|
Ti
|
V
|
Nb
|
|
最小值
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
|
最大值
|
0.2
|
0.5
|
1.7
|
0.035
|
0.035
|
0.3
|
0.5
|
0.3
|
0.1
|
0.012
|
0.2
|
0.15
|
0.07
|
|
鋼的牌號和化學成分(熔煉分析)應符合GB/T 700和GB/T 1591的規定。
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Q345A 機械性能
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
厚度（直徑、邊長）
|
抗拉強度
|
屈服點
|
斷后伸長率或延伸率
|
|
|
|
|
|
|
|
|
|
|
|
t
|
σb
|
σs
|
δ
|
|
|
|
|
|
|
|
|
|
|
|
mm
|
Mpa
|
Mpa
|
%
|
|
|
|
|
|
|
|
|
|
|
|
t≤16
|
470~630
|
≥345
|
≥20
|
|
|
|
|
|
|
|
|
|
|
|
16 < t ≤ 40
|
470~630
|
≥335
|
≥20
|
|
|
|
|
|
|
|
|
|
|
|
40＜t≤63
|
470~630
|
≥325
|
≥19
|
|
|
|
|
|
|
|
|
|
|
|
63＜t≤80
|
470~630
|
≥315
|
≥19
|
|
|
|
|
|
|
|
|
|
|
|
80＜t≤100
|
470~630
|
≥305
|
≥19
|
|
|
|
|
|
|
|
|
|
|
|
100＜t≤150
|
450~600
|
≥285
|
≥18
|
|
|
|
|
|
|
|
|
|
|
|
150＜t≤200
|
450~600
|
≥275
|
≥17
|
|
|
|
|
|
|
|
|
|
|
|
200＜t≤250
|
450~600
|
≥265
|
≥17
|
|
|
|
|
|
|
|
|
|
|
|
1、力學性能：
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
①厚度小于3mm的鋼板和鋼帶的抗拉強度和斷后伸長率應符合GB/T 700、GB/T 1591的規定，斷后伸長率允許比GB/T 700或GB/T 1591的規定降低5%(絕對值)。根據需方要求，鋼板和鋼帶的屈服強度可按GB/T 700、GB/T 1591的規定。
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
②厚度不小于3mm的鋼板和鋼帶的力學和工藝性能應符合GB/T 700、GB/T 1591的規定。
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
2、工藝性能：
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
鋼板和鋼帶應做180°彎曲試驗，試樣彎曲壓頭直徑應符合GB/T 700、GB/T 1591的規定。如供方能保證冷彎試驗合格，可不作檢驗。
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|